GW2003P High Wax Content, High Precision, Easy to Print and Cast, High-Precision Green Wax for Jewelry

Material Category

Fine Green Wax

Material Description

Ceramic-coated casting resin is a light-curing material that combines the advantages of both wax and resin. It is the best choice for conventional light-curing 3D printers. It has the easy-casting characteristics of wax and the high strength and toughness of resin, significantly improving the success rate of casting.
Print stable and reliable
It still retains the high strength characteristic of resin, making the printing more stable. The high toughness can achieve direct wax inlay without chipping the stone, thus simplifying the process flow.
Surface smooth and fine
Because of the wax's smoothing effect, the surface becomes smoother, while still having a high level of detail presentation, allowing the printed piece to better restore the design.
Burns without ash or residue
Because of the presence of wax, when heated, the wax disappears first to form honeycomb-shaped voids. When the resin expands due to heat, it will fill the voids first, reducing damage to the gypsum. The burning is very clean, without ash or residue, and the casting has no flaws.

Viscosity	260Mpa*s
Tensile Strength	8.8Mpa
Elongation at Break	2.35%
Flexural Strength	13.3Mpa
Flexural Modulus	23.1Mpa
Bending Strain	3.90%
Izod Impact-Notched	570J/m²
Density	1.08-1.13g/cm³
Hardness（Shore D）	58 Shore
Changing Temp	120-150℃

English

中文

GW2003P High Wax Content, High Precision, Easy to Print and Cast, High-Precision Green Wax for Jewelry